- Material composition: S235JR - DIN EN 10025
- Surface finish: Continuous hot-dip galvanized, approx. 70 µm - DIN EN 10346
- Material composition: S235JR - DIN EN 10025
- Surface finish: Continuous hot-dip galvanized, approx. 70 µm - DIN EN 10346
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 45 µm - DIN EN ISO 1461
- Material composition: S235JR - DIN EN 10025
- Surface finish: Continuous hot-dip galvanized, approx. 70 µm - DIN EN 10346
- Material composition: S250GD - DIN EN 10346
- Surface finish: Hot-dip galvanized, 45 µm - DIN EN ISO 1461
- Material composition: S235JR - DIN EN 10025
- Surface finish: Continuous hot-dip galvanized, approx. 70 µm - DIN EN 10346
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 45 µm - DIN EN ISO 1461
- Material composition: S250GD - DIN EN 10346
- Surface finish: Hot-dip galvanized, 45 µm - DIN EN ISO 1461
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 45 µm - DIN EN ISO 1461
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Profile: MQ-41-F
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Profile: MQ-41-F
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Profile: MQ-41-D-F
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Profile: MQ-72-F
MQN-F
- Product class: Standard
- Material composition: Bolt: grade 8.8 - DIN EN ISO 898, Plate: S235JR - DIN EN 10025, Nut: C4C - DIN EN 10263
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
MQN-HDG plus
- Product class: Premium
- Material composition: Bolt: M10 grade 8.8 - DIN ISO 898, Nut: C4C - DIN EN 10263, Plate: DD11 - DIN EN 10111
- Surface finish: Multi-layer coating – performance in salt spray test equal to hot-dip galvanizing
- Material composition: Nut: EN-GJMW-450-7 - DIN EN 1562, Plate: S235JR - DIN EN 10025, Plastic: PB
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: Wings: plastic PA, Nut: C4C - DIN EN 10263
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: Wings: plastic PA, Nut: QStE 380 TM, SEW 92
- Surface finish: Multi-layer coating
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: U-bolt: S235JRG2 - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
MF-FL-HDG
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 45 µm - DIN EN ISO 1461
- Material thickness: 6 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: Structural steel with minimum yield strength of 235 N/mm2
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: Steel grade 8.8
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: Steel grade 8.8
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: Steel grade 8
- Surface finish: Hot-dip galvanized
- Material composition: Structural steel with a minimum yield strength of 275 N/mm2 for the channel, 355 N/mm2 for the plate
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Profile: MC-3D-41
- Material composition: Structural steel with minimum yield strength of 235 N/mm2
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: Structural steel with minimum yield strength of 235 N/mm2
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: Structural steel with minimum yield strength of 235 N/mm2
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: Structural steel with minimum yield strength of 235 N/mm2
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: Structural steel with minimum yield strength of 235 N/mm2
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: Structural steel with minimum yield strength of 235 N/mm2
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: Structural steel with minimum yield strength of 235 N/mm2
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: Structural steel with minimum yield strength of 235 N/mm2
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: Structural steel with minimum yield strength of 235 N/mm2
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: Structural steel with minimum yield strength of 275 N/mm2
- Surface finish: Hot-dip galvanized, 65 µm - ASTM A123
- Material composition: Structural steel with minimum yield strength of 235 N/mm2
- Surface finish: Hot-dip galvanized, 65 µm - ASTM A123
- Material composition: QStE 380 TM - SEW 092
- Surface finish: Multi-layer coating, designed for corrosion environment category C3 according to ISO 9223
- Material composition: QStE 380 TM - SEW 092
- Surface finish: Multi-layer coating, designed for corrosion environment category C3 according to ISO 9223
- Material composition: DD11 MOD – HN 555-4, S235JR – EN10025-2
- Surface finish: Hot-dip galvanised, 75µm - DIN EN ISO 1461
- Material composition: Connector: DD11 MOD - HN 547, S235JR - DIN EN 10025; bolt: 8.8 grade steel; nut: 8 grade steel
- Surface finish: HDG: connector 55 µm - DIN EN ISO 1461; bolt, nut 45 µm - DIN EN ISO 1461
- Material composition: Connector: DD11 MOD - HN 547, S235JR - DIN EN 10025; backing plate, toothed plate: EN-GJMW-400-5 - DIN EN 1562, EN-GJMW-450-7 - DIN EN 1562; bolt: 8.8 grade steel; nut: 8 grade steel
- Surface finish: HDG: connector 55 µm - DIN EN ISO 1461; backing plate, toothed plate, bolt, nut 45 µm - DIN EN ISO 1461
- Material composition: Steel grade 8
- Surface finish: HDG: 45 µm - DIN EN ISO 1461
- Material composition: Connector: DD11 MOD - HN 547, S235JR - DIN EN 10025; bolt: 8.8 grade steel; nut: 8 grade steel
- Surface finish: HDG: connector 55 µm - DIN EN ISO 1461; bolt, nut 40 µm - DIN EN ISO 10684