- Material composition: S235JR - DIN EN 10025
- Surface finish: Continuous hot-dip galvanized, approx. 70 µm - DIN EN 10346
- Material composition: S235JR - DIN EN 10025
- Surface finish: Continuous hot-dip galvanized, approx. 70 µm - DIN EN 10346
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 45 µm - DIN EN ISO 1461
- Material composition: S235JR - DIN EN 10025
- Surface finish: Continuous hot-dip galvanized, approx. 70 µm - DIN EN 10346
- Material composition: S250GD - DIN EN 10346
- Surface finish: Hot-dip galvanized, 45 µm - DIN EN ISO 1461
- Material composition: S235JR - DIN EN 10025
- Surface finish: Continuous hot-dip galvanized, approx. 70 µm - DIN EN 10346
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 45 µm - DIN EN ISO 1461
- Material composition: S250GD - DIN EN 10346
- Surface finish: Hot-dip galvanized, 45 µm - DIN EN ISO 1461
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 45 µm - DIN EN ISO 1461
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Profile: MQ-41-F
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Profile: MQ-41-F
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Profile: MQ-41-D-F
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Profile: MQ-72-F
MQN-F
- Product class: Standard
- Material composition: Bolt: grade 8.8 - DIN EN ISO 898, Plate: S235JR - DIN EN 10025, Nut: C4C - DIN EN 10263
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
MQN-HDG plus
- Product class: Premium
- Material composition: Bolt: M10 grade 8.8 - DIN ISO 898, Nut: C4C - DIN EN 10263, Plate: DD11 - DIN EN 10111
- Surface finish: Multi-layer coating – performance in salt spray test equal to hot-dip galvanizing
- Material composition: Wings: plastic PA, Nut: C4C - DIN EN 10263
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: Wings: plastic PA, Nut: QStE 380 TM, SEW 92
- Surface finish: Multi-layer coating
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material composition: U-bolt: S235JRG2 - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
MF-FL-HDG
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 45 µm - DIN EN ISO 1461
- Material thickness: 6 mm
- Material composition: S235JR - DIN EN 10025
- Surface finish: Hot-dip galvanized, 56 µm - ASTM A153
- Material thickness: 4 mm